Production of carbide and hard-alloy mixture nanopowders with low-temperature plasma
https://doi.org/10.17073/1997-308X-2013-3-7-14
Abstract
The processes to produce nanosized tungsten carbide powders as well as other transition metal carbides have been investigated with the use of plasma-chemical reduction synthesis. The basic regularities of producing powders of specified dispersion and composition have been determined. Characteristic particle sizes of carbides are 40–80 nm. For the purpose of homogeneous WC–Со nanopowders mixture production with exact mass content, a technique of cobalt sedimentation onto tungsten carbide powder with simultaneous adding of retardant-carbides such as chromium, va- nadium, and tantalum carbides has been developed. The produced nanopowders have been examined with modern methods including high-reso- lution SEM and fractional gas analysis.
About the Authors
N. V. Isaeva
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
Yu. V. Blagoveshchensky
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
N. V. Blagoveshchenskaya
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
Yu. I. Melnik
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
A. V. Samokhin
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
N. V. Alekseyev
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
A. G. Astashov
Институт металлургии и материаловедения им. А. А Байкова (ИМЕТ) РАН, 119991, г. Москва, Ленинский пр-т, 49
Russian Federation
Russian Federation
References
1. Conner C. L. // Proc. 7 Inter. Tungsten Symp. (Goslar, Germany, Sept. 24–27. 1996). Р. 171–179.
2. McCandlish L. E., Kear B. H., Kim B. K. // Nanostruct. Mater. 1992. No 1. P. 119.
3. Pat. 5352269 (USA). Spray conversion process for the production of nanophase composite powders / S. J. Bhatia, B. H. Kear, L. E. McCandlish. 1994.
4. Pat. WO 2000029325 A1 (pat. DE19852459A1 (Germany)). Спо соб изготовления карбида вольфрама посредством карби дизации в газовой фазе / J. Bredthauer, G. Gille, B. Gries. 2000.
5. Guo S. // Proc. 16th Inter. Plansee Seminar. Tirol, Austria. HM17. 2005. Vol. 2.
6. Цветков Ю. В., Панфилов С. А. Низкотемпературная плазма в процессах восстановления. М.: Наука, 1980.
7. Пат. 2349424 (РФ). Способ получения порошков на основе карбида вольфрама / Ю. В. Благовещенский, А. В. Самохин, Ю. В. Цветков, Н. В. Алексеев. 2007.
8. Красовский П. В., Благовещенский Ю. В., Григорович К. В. // Неорган. материалы. 2008. Т. 44, No 9. С. 1074–1079.
9. Креймер Г. С., Эфрос Л. Д., Воронкова Е. А. // ЖТФ. 1952. Т. 22, No 5. С. 858–862.
Review
For citations:
Isaeva N.V., Blagoveshchensky Yu.V., Blagoveshchenskaya N.V., Melnik Yu.I., Samokhin A.V., Alekseyev N.V., Astashov A.G. Production of carbide and hard-alloy mixture nanopowders with low-temperature plasma. Powder Metallurgy аnd Functional Coatings (Izvestiya Vuzov. Poroshkovaya Metallurgiya i Funktsional'nye Pokrytiya). 2013;(3):7-14. (In Russ.) https://doi.org/10.17073/1997-308X-2013-3-7-14
Views:
1347
Email this article 