The Mechanism of Phase Formation and Peculiarities of Mechanochemical Synthesis of Chromium Carbide

https://doi.org/10.17073/1997-308X-2014-3-8-15

Abstract

There was investigated influence of mechanical activation in centrifugal planetary mill (during 9–43 min at relation of balls mass and material B : M = 20 : 1) and subsequent high-speed heating (~ 6 °C/s) on phase formation in the system of chromium–carbon. There was elucidated that incu- bation period of carbide forming during mechanosynthesis process correlated well with thinning of interlayer of chromium in rolls like particles until length of chromium’s diffusion path into carbon. There was demonstrated that not occurred any sufficient (> 1 kJ/mol) internal energy storage in the lattice of crystalline chromium and free surface of soot. There was confirmed diffusion character of carbide forming in the system of chromium – soot as in mechanosynthesis process, both at subsequent flash heating. 

About the Authors

O. N. Pripisnov
Национальный исследовательский технологический университет «МИСиС», 119049, г. Москва, В-49, Ленинский пр-т, 4
Russian Federation


E. V. Shelekhov
Национальный исследовательский технологический университет «МИСиС», 119049, г. Москва, В-49, Ленинский пр-т, 4
Russian Federation


S. I. Rupasov
Национальный исследовательский технологический университет «МИСиС», 119049, г. Москва, В-49, Ленинский пр-т, 4
Russian Federation


A. S. Medvedev
Национальный исследовательский технологический университет «МИСиС», 119049, г. Москва, В-49, Ленинский пр-т, 4
Russian Federation


References

1. Косолапова Т. Я. Карбиды. М.: Металлургия, 1968.

2. Loubiere S., Laurent C., Bonino J. P., Rousset A. // Mater. Res. Bull. 1998. Vol. 33. Р. 935–944.

3. Ермилов А.Г., Егорычев К.Н., Либенсон Г.А., Рупа- сов С.И. // Изв. вузов. Цв. металлургия. 1997. No 1. С. 53–61.

4. Ермилов А. Г., Сафонов В. В., Дорошко Л. Ф., Коля- кин А. В. // Там же. 2000. No 6. С. 55–60.

5. Maurice D., Courtney T. H. // Metal. Trans. A. 1994. Vol. 25A, No 1. P. 147–158.

6. Maurice D., Courtney T. H. // Ibid. 1995. Vol. 26A, No 9. P. 2431–2435.

7. Maurice D., Courtney T. H. // Ibid. P. 2437–2444.

8. Шелехов Е. В., Приписнов О. Н., Рупасов С. И. // Изв. вузов. Цв. металлургия. 2001. No 1. С. 29–33.

9. Шелехов Е. В., Приписнов О. Н., Рупасов С. И. // Изв. вузов. Цв. металлургия. 2001 No 6. С. 66–71.

10. Шелехов Е. В., Свиридова Т. А. // Металловедение и терм. обраб. металлов. 2000. No 8. С. 16–19.

11. Свиридова Т. А., Шевчуков А. П., Шелехов Е. В., Борисова П. А. // Физика металлов и металловедение. 2011. Т. 112, No 4. С. 378–392.

12. Шелехов Е. В., Свиридова Т. А. // Материаловедение. 2007. No 10. С. 13–22.


Review

For citations:


Pripisnov O.N., Shelekhov E.V., Rupasov S.I., Medvedev A.S. The Mechanism of Phase Formation and Peculiarities of Mechanochemical Synthesis of Chromium Carbide. Powder Metallurgy аnd Functional Coatings (Izvestiya Vuzov. Poroshkovaya Metallurgiya i Funktsional'nye Pokrytiya). 2014;(3):8-15. (In Russ.) https://doi.org/10.17073/1997-308X-2014-3-8-15

Views: 986


ISSN 1997-308X (Print)
ISSN 2412-8767 (Online)